KC Jones Plating: Zinc Nickel Plating, Zinc Plating, Electroless Nickel Plating |

Prevent premature part failure through engineered corrosion, friction and wear resistance.

Select permanent leakproof joints, and speed both production and assembly time.

Improve brand reputation with the most secure fasteners, screws and fittings.

KC Jones Plating Company

KC Jones has strived to advance the life and performance of parts for 65+ years, through surface engineering technology. Customers return time and again for well-crafted solutions: corrosion protection, wear resistance, furnace brazing and pre-applied adhesives.

PROPERTY	HIGH PHOS	MID PHOS	LOW PHOS	NICKEL BORON
% PHOSPHOROUS or BORON	10 – 13	7 – 9	1 – 3	0.2 – 1	3 – 5
DEPOSIT DENSITY Range (g/cm3)	7.6 – 7.9	8.0 – 8.2	8.6 – 8.8	8.8	8.25
PLATING DEPOSITION RATE (m/HR)	7.5 – 15	15 – 25	11 – 19	5 – 10	5 – 18
HARDNESS AS PLATED (HK100)	450 – 525	500 – 600	725 – 800	600 – 700	650 – 750
ROCKWELL C (Rc) HARDNESS CONVERSION* AS PLATED	41 – 46	45 – 51	57 – 61	51 – 56	54 – 59
HARDNESS HEAT TREATMENT (HK100)	850 – 950	850 – 1000	900 – 1100	500 – 600	1100 – 1200
ROCKWELL C (Rc) HARDNESS CONVERSION* AT HEAT TREATMENT	64 – 67	64 – 71	66 – 74	45 – 51	74 – 76
TABER WEAR INDEX AS PLATED (mg/1000 CYCLES-CS-10 WHEEL, 1000g LOAD)	22 – 24	16 – 20	7 – 12	7 – 9	8 – 15
TABER WEAR INDEX After HEAT TREATMENT (mg/1000 CYCLES-CS-10 WHEEL, 1000g LOAD)	10 – 14	10 – 12	6 – 10	7 – 9	3 – 10